ADD APT PolySurF HP
Mixture of acrylated mono-and di-phosphate ester
ADD APT
附着力促进剂/粘接剂 >> 磷酸盐
Adhesion promoter / Bonding agent >> Phosphate
阻燃剂 >> 磷型
Flame retardant / Fire retardant >> Phosphorus based
光触发剂
Photoinitiator
涂层 >> UV / 辐射线固化
Coatings >> UV / Radiation Curing
ADD APT PolySurF HP is a solvent free UV-curable additive. It can also act as a co-polymerisable anionic surfactant and/or adhesion promoter with flame retardant properties.
It is a proprietary mixture of Acrylated mono-and di-Phosphate ester; where the reactive Acrylate group is Methacrylate.
Emulsions for paints, lacquers, printing inks and adhesives 0.5 - 2.5 % wt. based on monomers
Flame retardant and adhesion promoter for UV curable systems ca. 1 - 2.5% wt. based on monomers
Easy to handle liquid
It is an effective flame retardant, which does not contain halogens.
Addition of approximately 4%, results in a final P content of the flame-retardant
polyester or polyacrylate of approx. 0.5 %.
It improves both the storage and mechanical stability of an emulsion system,
whereas grit building and foam formation is minimised.
No migration of the surfactant occurs after film formation
Paints and lacquers based on emulsions containing this “build-in” anionic
surfactant show improved wet-scrub resistance, improved adhesion to metal and
high yellowing resistance even after enamel application
The mono-phosphate ester can be reacted with emulsions containing polymers with
2 or more epoxy groups or with emulsions containing, for example,
Glycidyl(Meth)acrylate.
The di-phosphate ester affords some degree of crosslinking without gel formation.
Mixture of methacrylated mono-and di-phosphate ester. Used as a solvent free UV-curable additive for paints, lacquers and printing inks. Can be used as a co-polymerisable anionic surfactant and as an adhesion promoter with flame retardant properties. Offers easy handling. Improves storage and mechanical stability. Reduces grit building and foam formation. Gives improved wet-scrub resistance, improved adhesion to metal and high yellowing resistance even after enamel application.
Use level: 0.5-2.5 %wt based on monomers