ADD APT PolySurF HPH is a solvent-free UV-curable additive. It can also act as a polymerisable hydrophilic non-ionic surfactant and/or co-polymerisable plasticizer.
It is a proprietary mixture of Acrylated mono- and di-Phosphate ester; the mono-Phosphate ester being O-(EO)n>10-CH3 modified; where the reactive Acrylate group is Methacrylate
Emulsions for paints, lacquers, printing inks and adhesives
As surfactant: 0.5 - 2.5 % wt. based on monomers
Polymerisable Plasticizer for polyacrylates, polyesters, PVC
Levelling/Wetting agent and Adhesion Promoter for metal for UV curable systems
Easy to handle liquid
It imparts excellent Levelling/Wetting and improves adhesion to metal surfaces in
UV-curable systems.
It effectively improves the wetting of substrates like wood and metal as a monomer
but also when incorporated in an emulsion.
It improves both the storage and mechanical stability of an emulsion system,
whereas grit building and foam formation is minimised.
No migration of the non-ionic surfactant occurs after film formation
Paints and lacquers based on emulsions containing this “build-in” hydrophilic
non-ionic surfactant show improved wet-scrub resistance, improved adhesion to
metal and high yellowing resistance even after enamel application.
It has flame retardant properties and does not contain halogens.
The di-phosphate ester affords some degree of crosslinking without gel formation.
Mixture of methacrylated mono-and di-phosphate ester. Used as a solvent free UV-curable additive for paints, lacquers and printing inks. Can be used as a polymerisable hydrophilic non-ionic surfactant and a co-polymerisable plasticizer for polyacrylates, polyesters and PVC. Offers easy handling and very good levelling/wetting properties. Improves adhesion to metal surfaces in UV-curable systems, wetting of substrates like wood and metal and storage and mechanical stability. Reduces grit building and foam formation. Gives no migration of non-ionic surfactant, improved wet-scrub resistance, improved adhesion to
metal, high yellowing resistance even after enamel application, flame retardant properties and some degree of crosslinking without gel formation.
Use level: 0.5-2.5 %wt based on monomers.