ADD APT PolySurF HPL
Mixture of acrylated mono-and di-phosphate ester
ADD APT
阻燃剂 >> 磷型
Flame retardant / Fire retardant >> Phosphorus based
光触发剂
Photoinitiator
可塑剂 >> 磷酸盐
Plasticizer >> Phosphate
丙烯酸/丙烯酸盐树脂
Acrylic/Acrylate Resins
聚酯
Polyester
乙烯基
Vinyl
涂层 >> UV / 辐射线固化
Coatings >> UV / Radiation Curing
ADD APT PolySurF HPL is a solvent-free UV-curable additive. It can also act as a polymerisable lipophilic non-ionic surfactant and/or polymerisable plasticizer.
It is a proprietary mixture of Acrylated mono-and di-Phosphate ester: the mono-Phosphate ester being O-C12-C14 modified; where the reactive Acrylate group is Methacrylate.
Emulsions for paints, lacquers, printing inks and adhesives
As surfactant: 0.5 - 2.5 % wt. based on monomers
Flame retardant for unsaturated polyesters and polyacrylates polyesters and polyacrylates
Polymerisable Plasticizer for polyacrylates, polyesters, PVC
Flame retardant and Plasticizer for UV curable systems
Easy to handle liquid
It imparts excellent Levelling/Wetting and improves adhesion to metal surfaces in
UV-curable systems.
It is an effective flame retardant, which does not contain halogens.
Addition of approximately 5 % results in a final P content of the flame-retardant
polyester, polyacrylate or PVC of approx. 0.5 %.
It is an effective plasticizer. No plasticizer migration occurs after through-cure.
It improves both the storage and mechanical stability of an emulsion system, whereas
grit building and foam formation is minimised.
No migration of the non-ionic surfactant occurs after film formation
Paints and lacquers based on emulsions containing this “build-in” lipophilic
non-ionic surfactant show improved wet-scrub resistance, improved adhesion to
metal and high yellowing resistance even after enamel application.
The di-phosphate ester affords some degree of crosslinking without gel formation.
Mixture of methacrylated mono-and di-phosphate ester. Used as a solvent free UV-curable additive for paints, lacquers and printing inks. Can be used as a polymerisable lipophilic non-ionic surfactant, a flame retardant and a polymerisable plasticizer for UV curable systems. Offers easy handling and very good levelling/wetting properties. Improves adhesion to metal surfaces and storage and mechanical stability. Reduces grit building and foam formation. Gives no migration of non-ionic surfactant and plasticizer, improved wet-scrub resistance, improved adhesion to metal, high yellowing resistance even after enamel application and some degree of crosslinking without gel formation.
Use level: 0.5-2.5 %wt based on monomers.