Dow Corning 1
Silicone
Dow Corning
抗磨损性
Abrasion Resistance
流动/均化剂 >> 硅树脂
Flow / Levelling agent >> Silicone
底材表面处理剂, 混杂 >> 防凹陷剂
Surface conditioner, miscellaneous >> Anti-crater aid
底材表面处理剂, 混杂 >> 光泽控制
Surface conditioner, miscellaneous >> Gloss control
润湿剂/边缘润湿促进剂 >> 硅树脂
Wetting agent/ Wet edge enhancer >> Silicone
丙烯酸/丙烯酸盐树脂
Acrylic/Acrylate Resins
醇酸树脂
Alkyd Resins
氨基树脂
Amino Resins
纤维素树脂
Cellulosic Resins
环氧树脂
Epoxy Resins
涂层 >> 由溶剂生成
Coatings >> Solventborne
涂层 >> UV / 辐射线固化
Coatings >> UV / Radiation Curing
Dow Corning® 1
Additive
TYPICAL PROPERTIES
Specifications writers: These values are not intended for use in preparing specifications.
Please contact your local Dow Corning sales representative prior to writing specifications
on this product.
Parameter
Silicone additive for paints and coatings
Unit Value
APPLICATIONS
Air drying systems, alkyd resins, nitrocellulose and two component acid cured
alkyd systems such as alkyd/urea resins and p-toluensulfonic acid hardened
epoxies.
For use in solvent based paints for leather and lacquers for playing cards.
Stoving systems such as acrylic and alkyd/amino resins.
FEATURES
Limited miscibility with water at
room temperature
Recoatable when used as directed
Addition levels not critical
High flash point (120°C/248°F)
Low toxicity
Miscible with many solvents
Reduces cratering
Non-volatile
Improves flow out, increases gloss
and wetting
Imparts mar resistance and
abrasion resistance by reducing
surface friction
?
Improves film deaeration ?
Helps control pigment separation ?
Prevents pinholes, orange peel and
cell structure
?
HOW TO USE
Recommended addition level is 0.1%
to 0.5% Dow Corning 1 Additive
during the final thinning stage.
Applications: air drying systems, alkyd resins, nitrocellulose and two component acid cured alkyd systems such as alkyd/urea resins and p-toluensulfonic acid hardened epoxies. For use in solvent based paints for leather and lacquers for playing cards. Can be used in stoving systems such as acrylic and alkyd/amino resins.
Recoatable when used as directed. Miscible with many solvents. Reduces cratering. Non-volatile. Improves flow out, increases gloss and wetting. Imparts mar resistance and abrasion resistance by reducing surface friction. Improves film deaeration. Helps control pigment separation. Prevents pinholes, orange peel and cell structure.
Recommended usage level: 0.1% to 0.5% during the final thinning stage.